本文针对葛洲坝钟祥水泥公司附近工业废渣的分布，利用煤矸石、河沙、石灰石和磷渣四种工业废渣生产混凝土复合掺和料，借助粉磨设备、水泥胶砂强度试验、XRD(X射线衍射）分析等对工业废渣用作混凝土掺和料进行了系统的试验研究，寻找到最优的配合比。
关键字：工业废渣、混凝土、掺合料
Experimental study on composite admixture for concrete production by industrial waste residue
Chenshan
(China gezhouba group cement co. LTD wuhan 430000)
This paper is aimed at the distribution of industrial waste residue near gezhouba zhongxiang cement co,The concrete compound admixture was produced by using four kinds of industrial waste residue: coal gangue, river sand, limestone and phosphorus residue,By means of powder grinding equipment, strength test of cement sand and XRD(X-ray diffraction) analysis, the systematic experimental study on industrial waste slag used as concrete admixture was carried out, and the optimal mixture ratio was found.
Keywords: industrial waste residue, concrete, admixture
混凝土掺合料作为制备高性能混凝土必不可少的组分之一，它在改善混凝土的力学性能和耐久性能方面起着至关重要的作用，随着生产混凝土掺合料原材料粉煤灰的日益紧缺，急需开发一种原料充沛、生产工艺简单、生产成本低，生态环境影响小的混凝土掺合料生产方法，研究利用工业废渣生产混凝土掺合料并开发为有经济社会发展前景的新产品，具有重要的工业应用价值和社会效益。
1.实验
1.1原材料的选取
本文原材料选取葛洲坝钟祥水泥公司附近储备丰富的工业废渣，根据混凝土掺和料特性选择了四种工业废渣，依次为煤矸石、河沙、石灰石和磷渣，主要化学成分见表1：
表3中数据显示四种废渣通过不同方案混合，均能够满足二级混合材掺和料标准的要求，且成本远低于用粉煤灰。通过成本和性能的比较试验方案C1成本最低，性能较好。
3.试验结论
（1）用煤矸石、河沙、磷渣和石灰石四种材料配制的复合掺和料，能满足GB1596-2005《用于水泥和混凝土中的粉煤灰》性能要求，可以代替粉煤灰生产二级混凝土掺和料。
（2）从性能和成本综合情况来看，二级掺和料配方中采用河沙50%、煤矸石15%、石灰石5%及磷渣30%为最优配方，性价比最高。
参考文献：
[1]阮烔正,战高峰.如何开发混凝土活性掺合料[J].建筑技术开发,2000,27(2).
[2]欧阳东.混凝土矿物减水剂的概念、理论及其应用[J].混凝土,2000(1):44-47.
[3]阮烔正,梁锐,朱会荣,混凝土掺合料专业化生产技术[J].混凝土,2009(9).
[4]吴学礼,陈孟,朱蓓蓉.粉煤灰火山灰反应动力学的研究[J].建筑材料学报,2002,5(2):120-150.
[5]陈志源,李启令主编.土木工程材料[M].武汉理工大学出版社,2003.40-41.
论文作者:陈杉
论文发表刊物:《防护工程》2018年第27期
论文发表时间:2018/12/24
标签：混凝土论文; 废渣论文; 工业论文; 葛洲坝论文; 河沙论文; 石灰石论文; 掺合论文; 《防护工程》2018年第27期论文;