1.青岛理工大学土木工程学院 山东青岛 266033
摘要：硅酸盐水泥的水化会产生大量的Ca（OH）2，过多的Ca（OH）2使得混凝土的水泥砂浆呈现碱性，这为用盐酸强化废弃混凝土提供了理论基础。盐酸可以与混凝土表面的水泥砂浆反应生成可溶性的盐，新生成的盐可以填充再生骨料的孔隙，降低了再生骨料的孔隙率；通过反应，再生骨料表面的脆性砂浆减少降低了再生骨料的压碎指标与吸水率；反应过后，新拌水泥与再生骨料之间的粘结面更加牢固。
关键词：盐酸；再生粗骨料
Abstract：Portland cement hydration will produce a large number of Ca（OH）2，excessive Ca（OH）2 makes the cement mortar of concrete alkaline，which provides a theoretical basis for strengthening waste concrete with hydrochloric acid.Hydrochloric acid can react with cement mortar on the surface of concrete to form soluble salt，which can fill the pores of recycled aggregate and reduce the porosity of recycled aggregate；through the reaction，the brittle mortar on the surface of recycled aggregate reduces the crushing index and water absorption of recycled aggregate；after the reaction，fresh cement and fresh aggregate The bonding surface between recycled aggregate is more solid.
0 引 言
一般意义上的再生混凝土骨料是指废弃的混凝土经过清洗、破碎、筛选分级等处理后，按照一定的比例混合形成的骨料。根据再生骨料的颗粒大小分为再生粗骨料与再生细骨料，规范中定义粒径大于4.75mm的骨料为再生粗骨料。
1.试验概况
本试验再生粗骨料是学校实验室中用来做试验的混凝土试块经过清洗、破碎、筛选分级等处理后得到的。将其用浓度为3%的盐酸溶液浸泡3h，浸泡前后吸水率与压碎指标的数据如表1.1所示。
表1.1 盐酸浸泡前后再生粗骨料吸水率与压碎指标对比表
2.试验结果分析
浸泡前后再生粗骨料吸水率降低了20.30%，压碎指标降低了16.15%，表明盐酸能够提高再生粗骨料的物理性能。
3.结论
盐酸能够强化再生粗骨料的物理性能，但是能否改善再生粗骨料制成混凝土的力学性能尚待进一步研究。
论文作者:于凯1,朱伟超2
论文发表刊物:《基层建设》2018年第33期
论文发表时间:2018/12/20
标签：骨料论文; 吸水率论文; 盐酸论文; 混凝土论文; 砂浆论文; 指标论文; 压碎论文; 《基层建设》2018年第33期论文;