宣化钢铁集团有限责任公司 河北宣化 075100
摘要:宣钢一钢轧厂在冶炼低合金钢和普碳钢中用碳化硅(SiC)部分替代硅铁和增碳剂进行转炉合金化试验的生产实践表明,该工艺稳定性好,与同品种原脱氧合金化工艺相比，新脱氧合金化工艺使钢的化学成分内控率有所提高，吨钢成本降低1.70元/t钢,实现了良好的经济效益。
关键词:碳化硅;合金化;替代
Production Practice about SiC Instead of FeSi and Carburant
Zhao Guoying
Steel-making Plant,Xuanhua Iron and Steel Co.,Ltd,Xuanhua,075100
Abstract:Alloying experiments of the partial substitution of ferrosilicon and carburetant by SiC have been carried out in the first steelmaking workshop of XuanGang steelmaking plant in smelting low alloy steel and carbon-steel. Results show that this process has good stability and the internal control rate of thechemical compositions of the tested steel has been improved slightly, compared with the original deoxidizing alloying technology. At the same time, The production experiment achieved good economic benefit and the cost per ton has reduced 1.70 yuan.
Key words SiC； alloying； Substitution
前言:宣钢一钢轧厂拥有3座转炉，其中两座110t转炉和一座120t转炉。一钢轧厂生产低合金钢或普钢大量使用硅铁，随着锰铁、硅铁等合金供应的异常紧张，合金价格大幅攀升，导致了转炉炼钢成本不断上升。为降低成本，开发了碳化硅的功能，将其作为一种合金添加剂使用，部分替代价格昂贵的硅铁合金。2015年12月份进行了大规模生产试验，取得了较为满意的效果。
1 生产工艺及调整方案
1.1 原生产方式
宣钢一钢轧厂拥有600 t、900 t混铁炉各一座，两座110 t转炉，一座120 t转炉，以及三座方坯连铸机。2015年，宣钢一钢轧厂的产能为400万吨，冶炼钢种有低合金系列(如HRB335，HRB400等)、普碳钢、优质碳素钢、焊丝钢、优质带钢、制丝钢等11个系列，其中低合金钢和普碳钢所占比列为40%，约160万吨。长期以来一钢轧厂冶炼低合金系列和普碳钢的合金方式见表1。
随机抽取新方式2个炉号钢材(HRB400-2)进行了高、低倍检验。低倍检验结果，中心疏松最大为1级，未发现其它缺陷；高倍检验结果，最大夹杂物级别为2.5级，组织和晶粒度与未使用碳化硅的钢种基本相同。综合结果表明，钢材内部组织正常，质量良好。
2.2.3 成本效益分析
根据2015年12月宣钢一钢轧厂使用合金成本计算出，使用碳化硅后吨钢合金成本可减少1.70元/t钢按照一钢轧厂生产低合金钢和普碳钢160万吨/年，可节省成本272万元/年。
3 结论
（1)使用碳化硅部分替代硅铁和增碳剂后，钢的成分稳定，性能没有降低，满足了调整合金方案原则。
（2)使用碳化硅部分替代硅铁和增碳剂是一种节约成本且切实可行的工艺，吨钢成本降低1.70元/t钢，每年为宣钢增加效益272万元。
参考文献：
[1]李永刚,赵红亮,黄道昌,等.转炉应用碳化硅合金化的生产实践[J].炼钢,2006.12:8-10.
[2]王印强.碳化硅在炼钢合金化过程中的行为及效果[J].河北冶金,1995(4):28-31．
作者简介：
赵国英(1967.07-)，男，高级工程师,河北钢铁集团宣钢公司一钢轧厂；
论文作者:赵国英
论文发表刊物:《防护工程》2017年第10期
论文发表时间:2017/9/14
标签：合金论文; 碳化硅论文; 转炉论文; 成本论文; 硅铁论文; 宣钢论文; 宣化论文; 《防护工程》2017年第10期论文;